Superhydrophobic Fabrics Produced by Electrospinning and Chemical Vapor Deposition
Citations Over TimeTop 1% of 2005 papers
Abstract
A versatile method to produce superhydrophobic fabrics by combining electrospinning and initiated chemical vapor deposition (iCVD) is reported. In this study, poly(caprolactone) (PCL) was first electrospun and then coated with a thin layer of hydrophobic polymerized perfluoroalkyl ethyl methacrylate (PPFEMA) by iCVD. The hierarchical surface roughness inherent in the PCL electrospun mats and the extremely low surface free energy of the coating layer obtained by iCVD yields stable superhydrophobicity with a contact angle of 175° and a threshold sliding angle less than 2.5° for a 20 mg droplet. This PPFEMA-coated PCL mat was also shown to exhibit at least “grade 8” oleophobicity. Hydrophobicity was demonstrated to increase monotonically with a reduction in diameter among bead-free fibers and with the introduction of a high density of relatively small diameter beads. The systematic effect of fiber morphology on superhydrophobicity was also investigated theoretically and experimentally using both beaded and bead-free fibers with diameters ranging from 600 to 2200 nm.
Related Papers
- → Stability of the hydrophilic and superhydrophobic properties of oxygen plasma-treated poly(tetrafluoroethylene) surfaces(2013)68 cited
- → Surface wettability and energy effects on the biological performance of poly-3-hydroxybutyrate films treated with RF plasma(2016)42 cited
- → One-step deposition of stable superhydrophobic coatings with controllable wettability(2021)2 cited
- → Facile Fabrication of Super-Hydrophobic Surfaces by Spray PTFE(2015)
- Preparation of polymeric function film with different wettability(2009)