Rigid-Rod Poly(phenylenesulfonic acid) Proton Exchange Membranes with Cross-Linkable Biphenyl Groups for Fuel Cell Applications

Citations Over TimeTop 10% of 2012 papers

Abstract

Biphenyl was grafted on rigid-rod aromatic poly(p-phenylenesulfonic acids) (IEC ∼ 8 mequiv g–1) to generate cross-linkable polyelectrolytes. Cross-linking conditions and film properties before and after cross-linking were studied. Films equilibrated between 20 and 30% relative humidity (RH) had tensile moduli of 2 to 1 GPa and broke at 5 to 9% elongation. The moduli decreased as RH increased and dropped drastically at high humidity if the films were not cross-linked. Grafted films had conductivities at 80 °C 4–5 times that of Nafion NR-212 over the whole relative humidity range even after cross-linking. The sample reported in detail here had a conductivity of 0.10 S cm–1 at 120 °C and 30% RH. As is usual for this class of materials, even after the loss of 24% of starting sulfonic acid groups by grafting and cross-linking, ionic conductivity was high at low humidity. A membrane electrode assembly (MEA) prepared with this rigid-rod poly(phenylenesulfonic acid) proton exchange membrane and tested in a fuel cell exhibited performance and properties similar to those of Nafion NR-212 films. The power density was ∼95% of that of the Nafion MEA over the operating range in spite of relatively high hydrogen crossover due to the presence of nanocracks in the membrane.

Related Papers

• → Responsive polyelectrolyte multilayers(2007)124 cited
• → Polyelectrolyte Gels-Fundamentals and Applications(2006)89 cited
• → Pore network modeling of cathode catalyst layer of proton exchange membrane fuel cell(2012)42 cited
• → Weak Polyelectrolyte Brushes as Substrates for the Formation of Surface-Attached Polyelectrolyte−Polyelectrolyte Complexes and Polyelectrolyte Multilayers(2005)26 cited
• Experimental Study on Confined Swelling Characteristic of Redbed Mudstone in Chongqing(2015)