Universal Phenomenology of Symmetric Diblock Copolymers near the Order–Disorder Transition

Citations Over TimeTop 10% of 2015 papers

Abstract

We present a simulation study of how properties of symmetric diblock copolymers depend on the invariant degree of polymerization N̅, focusing on the vicinity of the order–disorder transition (ODT). Results from several coarse-grained simulation models are combined to cover a range of N̅ ≃ 200–8000 that includes most of the experimentally relevant range. Results are presented for the free energy per chain, the value of χeN at the ODT, the latent heat of transition, the layer spacing, the composition profile, and compression modulus in the ordered phase. Universality (i.e., model independence) is demonstrated by showing that equivalent results for all properties are obtained from corresponding thermodynamic states of different simulation models. Corresponding states of symmetric copolymers are states with equal values of the parameters χeN and N̅, where χe is an effective Flory–Huggins interaction parameter and N is a degree of polymerization. The underlying universality becomes apparent, however, only if data are analyzed using an adequate estimate of χe, which we obtain by fitting the structure factor in the disordered state to recent theoretical predictions. The results show that behavior near the ODT exhibits a different character at moderate and high values of N̅, with a crossover near N̅ ≃ 104. Within the range N̅ ≲ 104 studied here, the ordered and disordered phases near the ODT both contain strongly segregated domains of nearly pure A and B, in contrast to the assumption of weak segregation underlying the Fredrickson–Helfand (FH) theory. In this regime, the FH theory is inaccurate and substantially underestimates the value of χeN at the ODT. Results for the highest values of N̅ studied here agree reasonably well with FH predictions, suggesting that the theory may be accurate for N̅ ≳ 104. Self-consistent field theory (SCFT) grossly underestimates (χeN)ODT for modest N̅ because it cannot describe strong correlations in the disordered phase. SCFT is found, however, to yield accurate predictions for several properties of the ordered lamellar phase.

Related Papers

• → Synthesis of copolymers. I. Copolymers of styrene and of α‐methylstyrene(1972)12 cited
• → Anionic copolymerization of α,ω-dihydroxyoligodimethylsiloxane with organocyclosiloxanes(2008)2 cited
• → Anionic Copolymerization of α-Methylstyrene and 2, 3-Dimethylbutadiene(1972)2 cited
• STUDY ON COPOLYMERIZATION OF D_3~F, D_4(2002)
• Copolymerization of N-vinylformamid and N-vinylcaprolactam(2006)