Preparation of Chitin/Polystyrene Hybrid Materials by Efficient Graft Copolymerization Based on Mercaptochitin
Citations Over TimeTop 25% of 1996 papers
Abstract
Graft copolymerization of styrene onto mercaptochitin has been examined. Chitin was first tosylated to give tosylchitin, which was subsequently transformed into mercaptochitin. Athough the graft copolymerization was carried out in suspension, it proceeded efficiently to give chitin derivatives having polystyrene branches, a novel type of hybrid materials composed of a natural polysaccharide and a synthetic polymer. Under appropriate conditions, the grafting percentage reached 970%, indicating the high efficiency of the mercaptochitin as an initiator for the polymerization of styrene. The resulting graft copolymers exhibited glass transition phenomena at 115 °C and showed high swelling in organic solvents as a result of the introduction of polystyrene branches. Hydrolytic degradation of the chitin main chain allowed the isolation of the side chains, and the polystyrene isolated from the graft copolymer with a grafting percentage of 940% had Mn, Mw, and Mw/Mn values of 9.74 × 104, 2.55 × 105, and 2.62. These values indicate that the ratio of the mercapto groups actually used for initiating graft copolymerization was 4%, and a polystyrene chain attached on average to every 45 pyranose units.
Related Papers
- → Catalytic degradation of polystyrene into styrene and a design of recyclable polystyrene with dispersed catalysts(2000)172 cited
- → Plastics Based on Styrene(2016)22 cited
- → Effect of Styrene Monomer on the Fluorescence Properties of Polystyrene(1962)64 cited
- → Thermolysis of polystyrene(1995)18 cited
- In-situ emulsion polymerization of styrene in the presence of nano-SiO_2(2004)