Crystallization Kinetics as a Probe of the Dynamic Network in Lightly Sulfonated Syndiotactic Polystyrene Ionomers

Citations Over TimeTop 21% of 1996 papers

Abstract

The effect of alkali metal counterion type on the crystallization kinetics of sulfonated syndiotactic polystyrene with ion contents of 1.4 mol % was investigated. For crystallization temperatures less than 180 °C, the rate of crystallization was independent of counterion type. In contrast, for temperatures greater than 180 °C, the rate of crystallization increased with increasing counterion size. Since the glass transition and melting temperatures were found to be constant for all counterion types, the variations in crystallization behavior were attributed to differences in chain diffusion within the dynamic network of electrostatic cross-links. At low temperatures, the rate of ion-hopping is slow for all of the counterion forms relative to the rate of crystallization, and thus crystal growth occurred in the presence of kinetically stable cross-links. At high temperatures, chain diffusion is controlled by the ion-hopping process, and the kinetics of crystallization become influenced by the strengths of ionic interactions. Between 180 and 215 °C, the rate of crystallization was found to be inversely proportional to the ionic radii of the counterions. As the activation energy for ion-hopping increased with decreasing counterion size, longer periods of time were required to achieve the same degree of crystallinity.

Related Papers

• → Some aspects of nonisothermal crystallization of polymers. I. Relationship between crystallization temperature, crystallinity, and cooling conditions(1972)446 cited
• → Kinetics of nonisothermal crystallization of Cs2O–Fe2O3–P2O5 glasses(2010)8 cited
• → Numerical Simulation of Crystallization Morphological Evolution Under Nonisothermal Conditions(2008)8 cited
• → Crystallization of a Pelletized High-Crystallinity SAPO-11 Molecular Sieve with a Hierarchical Pore Structure(2020)1 cited
• Progress in Polymer Crystallization Induced by Low-dimensional Carbon Nanofiller(2011)