Modifying a Polystyrene/Poly(methyl methacrylate) Interface with Poly(styrene-co-methyl methacrylate) Random Copolymers

Citations Over TimeTop 10% of 1997 papers

Abstract

Joints of polystyrene (PS) and poly(methyl methacrylate) (PMMA) modified with ∼50 nm of poly(styrene-co-methyl methacrylate) random copolymer [P(S-ran-MMA)] were investigated. Copolymers having styrene compositions of fS = 0.48 and fS = 0.73 were used. Transmission electron microscopy reveals that the copolymers phase separate to form a distinct layer at the joint such that there is an interface with each homopolymer. Interfacial fracture toughness measurements, using the asymmetric double cantilever beam geometry, show a strong effect of the PS to PMMA sheet thickness ratio; that is, the phase angle influences the measured interfacial toughness. Reflection infrared spectroscopy on fracture surfaces indicates that the crack propagates at or near the PS/copolymer interface for all thickness ratios and for both copolymers. In-plane crazing was not observed in front of the crack tip for these systems. Rather, strengthening appears to be exclusively a consequence of oblique crazes in the more compliant PS sheet which form at 45° or 135° relative to the crack direction. Joints modified with P(S0.73-ran-MMA) exhibit denser oblique crazes than those modified with P(S0.48-ran-MMA), resulting in a higher measured fracture toughness at all sheet thickness ratios or phase angles.

Related Papers

• → Review of the biological response to a novel bone cement containing poly(ethyl methacrylate) and n-butyl methacrylate(1998)90 cited
• → Structural design and characterization of tricycloalkyl-containing methacrylate with methyl methacrylate copolymers(2021)13 cited
• → Research on the Influence of Stiffness of Copolymer(N-Tert-octylacrylamide/Acrylic acid/Methyl methacrylate/Butylaminoethyl Methacrylate/Hydroxypropyl Methacrylate) by Methyl Methacrylate and N-Tert-Octylacrylamide(2012)1 cited
• → Organotin polymers—I. Copolymerization parameters of tributyltin methacrylate with methyl methacrylate, propyl methacrylate and butyl methacrylate(1979)48 cited
• → Monomer Reactivity Ratios for the Copolymerization of p-lsopropylstyrene with Styrene and Methyl Methacrylate(1969)3 cited