Comparison of the Coil-to-Globule and the Globule-to-Coil Transitions of a Single Poly(N-isopropylacrylamide) Homopolymer Chain in Water

Citations Over TimeTop 10% of 1998 papers

Abstract

Using a newly prepared nearly monodisperse (Mw/Mn < 1.05) high molar mass (Mw = 1.3 × 107 g/mol) poly(N-isopropylacrylamide) (PNIPAM) sample, we successfully, for the first time, made the conformation of individual PNIPAM chains change from a coil to a fully collapsed thermodynamically stable single chain globule and then back to a coil in an extremely dilute aqueous solution (∼6.7 × 10-7 g/mL). The average chain density in the globule state is ∼0.34 g/mL, close to 0.40 g/cm3 predicted on the basis of a space-filling model, indicating that the globule still contains ∼66% water even in its fully collapsed state. At a given temperature around the lower critical solution temperature, the chains are smaller in the globule-to-coil transition than in the coil-to-globule transition, revealing that the coil-to-globule transition is an irreversible process. The hysteresis can be attributed to the formation of intrachain structures, presumably the intrachain hydrogen bonding, in the globule state. We confirmed the existence of the crumpled coil and the molten globule states between the random coil and the collapsed globule states. The coil-to-crumpled coil transition can be reasonably described by the Birshtein and Pryamitsyn theory.

Related Papers

• → Polydispersity index of polymers revealed by DOSY NMR(2011)129 cited
• → Quantifying the Heterogeneity of Chemical Structures in Complex Charged Polymers through the Dispersity of Their Distributions of Electrophoretic Mobilities or of Compositions(2015)20 cited
• → Contribution of the polymer standards’ polydispersity to the observed band broadening in size-exclusion chromatography(2003)21 cited
• → Influence of the dispersity and molar mass distribution of conjugated polymers on the aggregation type and subsequent chiral expression(2023)4 cited
• → Quasielastic light scattering as a method for determining the distribution of relaxation times in a polymer system(1992)7 cited