Growth Mechanism of Poly(divinylbenzene) Microspheres in Precipitation Polymerization
Citations Over TimeTop 10% of 1999 papers
Abstract
The residual surface vinyl groups in poly(divinylbenzene) microspheres prepared by precipitation polymerization in acetonitrile were converted to hexyl groups by treatment with n-butyllithium and to ethyl groups by catalytic hydrogenation in the presence of Wilkinson's catalyst. These modified particles and unmodified particles were used as seeds in separate precipitation polymerizations of divinylbenzene in acetonitrile, under identical conditions. Only the unmodified seeds were able to capture the oligomers formed and grow without secondary initiation. Both the butylated and the hydrogenated samples showed extensive secondary initiation instead of seed particle growth. These results demonstrate that precipitation polymerization of divinylbenzene in near-ϑ solvents is an entropic precipitation, involving radical reactions between the macromonomer particles and newly formed oligomers. These results further imply that the growing particles are autostabilized by the transient solvent-swollen gel layer on their surfaces, formed by a recently captured oligomer.
Related Papers
- → Effect of the polymerization parameters on the morphology and spherical particle size of poly(styrene-co-divinylbenzene) prepared by precipitation polymerization(2004)42 cited
- → Size and uniformity variation of poly(MMA-co-DVB) particles upon precipitation polymerization(2004)25 cited
- → Production of hollow particles by suspension polymerization of divinylbenzene with nonsolvent(2004)13 cited
- → Production of hollow particles by suspension polymerization of divinylbenzene with nonsolvent(2004)1 cited
- → Preparation of polystyrene by a free radical polymerization process(1998)