High-Aspect-Ratio Perpendicular Orientation of PS-b-PDMS Thin Films under Solvent Annealing
Citations Over TimeTop 10% of 2012 papers
Abstract
A perpendicular orientation of high-aspect-ratio polystyrene-block-polydimethylsiloxane (PS-b-PDMS) cylindrical and lamellar PDMS microdomains was achieved by solvent annealing and then slowly drying thick PS-b-PDMS films. Perpendicularly oriented microdomains occurred throughout the film thickness, except at the air interface, where a layer of in-plane microdomains formed due to the surface energy difference between PS and PDMS. In contrast, thermal annealing produced in-plane orientation throughout the film thickness. The solvent-annealed perpendicular orientation was observed for cylindrical morphology PS-b-PDMS of 16 and 45 kg/mol, where PDMS is the minority block, and lamellar PS-b-PDMS of 43 kg/mol. To obtain fully perpendicular microdomain patterns, a nonselective high-powered 450 W CF4/O2 reactive ion etching process was performed to remove the top layer of the films. Substrate patterning using electron beam lithography produced local registration of 17 nm period hexagonal cylinder patterns.
Related Papers
- → Print your own membrane: direct rapid prototyping of polydimethylsiloxane(2014)161 cited
- → 3D reactive inkjet printing of polydimethylsiloxane(2017)63 cited
- → Observation of chemically protected polydimethylsiloxane: towards crack-free PDMS(2017)32 cited
- → Perforated membrane method for fabricating three-dimensional polydimethylsiloxane microfluidic devices(2008)52 cited
- A novel method for fabricating polydimethylsiloxane microfluidic chip master molds(2009)