Ultrafast Electronic Relaxation and Charge-Carrier Localization in CdS/CdSe/CdS Quantum-Dot Quantum-Well Heterostructures
Citations Over TimeTop 13% of 2006 papers
Abstract
The relaxation and localization times of excited electrons in CdS/CdSe/CdS colloidal quantum wells were measured using subpicosecond spectroscopy. HRTEM analysis and steady-state PL demonstrate a narrow size distribution of 5-6 nm epitaxial crystallites. By monitoring the rise time of the stimulated emission as a function of pump intensity, the relaxation times of the electron from the CdS core into the CdSe well are determined and assigned. Two-component rise times in the stimulated emission are attributed to intraband relaxation of carriers generated directly within the CdSe well (fast component) and charge transfer of core-localized carriers across the CdS/CdSe interface (slow component). This is the first reported observation of simultaneous photon absorption in the core and well of a quantum-dot heterostructure. With increasing pump intensity, the charge-transfer channel between the CdS core CdSe well contributes less to the stimulated emission signal because of filling and saturation of the CdSe well state, making the interfacial charge-transfer component less efficient. The interfacial charge-transfer time of the excited electron was determined from the slow component of the stimulated emission build-up time and is found to have a value of 1.2 ps.
Related Papers
- → La2MgTiO6:Bi3+/Mn4+ photoluminescence materials: Molten salt preparation, Bi3+ → Mn4+ energy transfer and thermostability(2020)21 cited
- → Photoluminescence of porous Si, oxidized then deoxidized chemically(1992)109 cited
- → Cross-sectional HRTEM study of Si(5 5 12) reconstructed surface(2002)23 cited
- → Study of delocalized and localized states in ZnSeO layers with photoluminescence, micro-photoluminescence, and time-resolved photoluminescence(2019)7 cited
- → Ballistic effect and new concept of Si wire photoluminescence(2003)1 cited