Toward Intrinsic Graphene Surfaces: A Systematic Study on Thermal Annealing and Wet-Chemical Treatment of SiO2-Supported Graphene Devices
Citations Over TimeTop 1% of 2011 papers
Abstract
By combining atomic force microscopy and trans-port measurements, we systematically investigated effects of thermal annealing on surface morphologies and electrical properties of single-layer graphene devices fabricated by electron beam lithography on silicon oxide (SiO(2)) substrates. Thermal treatment above 300 °C in vacuum was required to effectively remove resist residues on graphene surfaces. However, annealing at high temperature was found to concomitantly bring graphene in close contact with SiO(2) substrates and induce increased coupling between them, which leads to heavy hole doping and severe degradation of mobilities in graphene devices. To address this problem, a wet-chemical approach employing chloroform was developed in our study, which was shown to enable both intrinsic surfaces and enhanced electrical properties of graphene devices. Upon the recovery of intrinsic surfaces of graphene, the adsorption and assisted fibrillation of amyloid β-peptide (Aβ1-42) on graphene were electrically measured in real time.
Related Papers
- → Fabrication of three-dimensional graphene foam with high electrical conductivity and large adsorption capability(2014)93 cited
- → A light-weight free-standing graphene foam-based interlayer towards improved Li-S cells(2019)48 cited
- → Graphene grown by chemical vapor deposition on metal foams(2020)5 cited
- → Graphene foam as an anode for high-rate Li-ion batteries(2011)14 cited
- → Synthesis and characterization of three-dimensional graphene foams by chemical vapor deposition(2017)1 cited