Shape and Composition-Controlled Platinum Alloy Nanocrystals Using Carbon Monoxide as Reducing Agent

Citations Over TimeTop 1% of 2011 papers

Abstract

The shape of metal alloy nanocrystals plays an important role in catalytic performances. Many methods developed so far in controlling the morphologies of nanocrystals are however limited by the synthesis that is often material and shape specific. Here we show using a gas reducing agent in liquid solution (GRAILS) method, different Pt alloy (Pt-M, M = Co, Fe, Ni, Pd) nanocrystals with cubic and octahedral morphologies can be prepared under the same kind of reducing reaction condition. A broad range of compositions can also be obtained for these Pt alloy nanocrystals. Thus, this GRAILS method is a general approach to the preparation of uniform shape and composition-controlled Pt alloy nanocrystals. The area-specific oxygen reduction reaction (ORR) activities of Pt(3)Ni catalysts at 0.9 V are 0.85 mA/cm(2)(Pt) for the nanocubes, and 1.26 mA/cm(2)(Pt) for the nanooctahedra. The ORR mass activity of the octahedral Pt(3)Ni catalyst reaches 0.44 A/mg(Pt).

Related Papers

• → Simultaneous control of nanocrystal size and nanocrystal-nanocrystal separation in CdS nanocrystal assembly(2005)55 cited
• → Manipulating the Charging Energy of Nanocrystal Arrays(2005)37 cited
• → A Study of Surface Oxides on Platinum Electrodes(1964)48 cited
• → Platinum on a sulfated zirconia surface: effects and interactions(1996)12 cited
• → Development of the Analytical Method of Iron through Optimization Reducing Agent Ability of Iron (III) to Iron(II)(2020)