In-situ X-ray Absorption Study of Evolution of Oxidation States and Structure of Cobalt in Co and CoPt Bimetallic Nanoparticles (4 nm) under Reducing (H2) and Oxidizing (O2) Environments
Citations Over TimeTop 10% of 2011 papers
Abstract
In-situ near edge X-ray absorption fine structure spectroscopy was performed to monitor the oxidation states of Co and CoPt nanoparticles (NPs) of 4 nm size in the presence of H(2) and O(2) in the pressure range of 1 bar and 36 Torr respectively. Platinum helps the rapid reduction of cobalt oxides in hydrogen at a rather low temperature (38 °C). In addition, reversible changes of the oxidation states of cobalt in the Co and CoPt NPs as a function of cycling oxygen pressure (in the range of millitorr to 36 Torr) are quantified and compared. The role of Pt in the process of Co reducing and oxidizing was explored. Our findings permit the prediction of the cobalt oxidation states as the reaction conditions are altered. The experimental results also suggest the presence of tetrahedral structure of Cobalt oxide that differs from the Co(3)O(4) spinel structure.
Related Papers
- → Comparative analysis of XANES and EXAFS for local structural characterization of disordered metal oxides(2021)28 cited
- → Investigation of Co nanoparticles with EXAFS and XANES(2004)75 cited
- → Determination of the Mo surface environment of Mo/TiO2 catalysts by EXAFS, XANES and PCA(1992)43 cited
- → Effects of Precursor Composition on the Local Structure of Cu Dispersed on Mesoporous Silica: A Detailed X-ray Absorption Spectroscopy Study(2004)37 cited
- → Investigation of the ‘‘join’’ between the near edge and extended x-ray absorption fine structure(1990)21 cited