Thermoelectric Behavior of Segregated-Network Polymer Nanocomposites
Citations Over TimeTop 10% of 2008 papers
Abstract
Segregated-network carbon nanotube (CNT)-polymer composites were prepared, and their thermoelectric properties were measured as a function of CNT concentration at room temperature. This study shows that electrical conductivity can be dramatically increased by creating a network of CNTs in the composite, while the thermal conductivity and thermopower remain relatively insensitive to the filler concentration. This behavior results from thermally disconnected, but electrically connected, junctions in the nanotube network, which makes it feasible to tune the properties in favor of a higher thermoelectric figure of merit. With a CNT concentration of 20 wt %, these composites exhibit an electrical conductivity of 4800 S/m, thermal conductivity of 0.34 W/m x K and a thermoelectric figure of merit (ZT) greater than 0.006 at room temperature. This study suggests that polymeric thermoelectrics are possible and provides the basis for further development of lightweight, low-cost, and nontoxic polymer composites for thermoelectric applications in the future.
Related Papers
- → Strongly Correlated Properties and Enhanced Thermoelectric Response in Ca3Co4−xMxO9 (M = Fe, Mn, and Cu)(2009)145 cited
- → Improvement of the thermoelectric characteristics of Fe-doped misfit-layered Ca3Co4−xFexO9+δ (x=, 0.05, 0.1, and 0.2)(2006)101 cited
- → Effect of Manganese Dioxide Nanorods on the Thermoelectric Properties of Cement Composites(2018)73 cited
- → Connectivity-driven bi-thermoelectricity in heteroatom-substituted molecular junctions(2018)33 cited
- → Influence of the sheet metal Seebeck coefficient on wear detection based on thermoelectric measurement(2021)1 cited