Raman Spectroscopy of Ripple Formation in Suspended Graphene
Citations Over TimeTop 10% of 2009 papers
Abstract
Using Raman spectroscopy, we measure the optical phonon energies of suspended graphene before, during, and after thermal cycling between 300 and 700 K. After cycling, we observe large upshifts ( approximately 25 cm(-1)) of the G band frequency in the graphene on the substrate region due to compression induced by the thermal contraction of the underlying substrate, while the G band in the suspended region remains unchanged. From these large upshifts, we estimate the compression in the substrate region to be approximately 0.4%. The large mismatch in compression between the substrate and suspended regions causes a rippling of the suspended graphene, which compensates for the change in lattice constant due to the compression. The amplitude (A) and wavelength (lambda) of the ripples, as measured by atomic force microscopy, correspond to an effective change in length Deltal/l that is consistent with the compression values determined from the Raman data.
Related Papers
- → The effect of substrates on the Raman spectrum of graphene: Graphene- on-sapphire and graphene-on-glass(2007)250 cited
- → Orthotropic friction at the edges and interior of graphene and graphene fluoride and frictional anisotropy of graphene at the nanoscale(2021)1 cited
- A natural advantage? Using mined graphite to make graphene(2013)
- Synthesis and Characterisation of Graphene Single Sheets(2012)
- Unique synthesis of graphene-based materials for clean energy and biological sensing applications(2012)