Synthesis of Well-Ordered COF Monolayers: Surface Growth of Nanocrystalline Precursors versus Direct On-Surface Polycondensation

Citations Over TimeTop 10% of 2011 papers

Abstract

Two different straightforward synthetic approaches are presented to fabricate long-range-ordered monolayers of a covalent organic framework (COF) on an inert, catalytically inactive graphite surface. Boronic acid condensation (dehydration) is employed as the polymerization reaction. In the first approach, the monomer is prepolymerized by a mere thermal treatment into nanocrystalline precursor COFs. The precursors are then deposited by drop-casting onto a graphite substrate and characterized by scanning tunneling microscopy (STM). While in the precursors monomers are already covalently interlinked into the final COF structure, the resulting domain size is still rather small. We show that a thermal treatment under reversible reaction conditions facilitates on-surface ripening associated with a striking increase of the domain size. Although this first approach allows studying different stages of the polymerization, the direct polymerization, that is, without the necessity of preceding reaction steps, is desirable. We demonstrate that even for a comparatively small diboronic acid monomer a direct thermally activated polymerization into extended COF monolayers is achievable.

Related Papers

• → Structural ordering of ω-ferrocenylalkanethiol monolayers on Au(111) studied by scanning tunneling microscopy(2009)17 cited
• → Mixed SAMs of backbone-functionalized tribenzotriquinacenes and alkanethiols: Synthesis, preparation and STM-investigations(2015)10 cited
• → Scanning tunneling microscopy of locally derivatized self-assembled organic monolayers(2003)3 cited
• CYCLIC VOLTAMMETRY STUDY OF SELF-ASSEMBLED LAYER ON SILVER(2006)
• Formation process and topography characteristics of OTS self-assembled monolayers(2002)