Stretching and Breaking of Ultrathin MoS₂

Citations Over TimeTop 1% of 2011 papers

Abstract

We report on measurements of the stiffness and breaking strength of monolayer MoS(2), a new semiconducting analogue of graphene. Single and bilayer MoS(2) is exfoliated from bulk and transferred to a substrate containing an array of microfabricated circular holes. The resulting suspended, free-standing membranes are deformed and eventually broken using an atomic force microscope. We find that the in-plane stiffness of monolayer MoS(2) is 180 ± 60 Nm(-1), corresponding to an effective Young's modulus of 270 ± 100 GPa, which is comparable to that of steel. Breaking occurs at an effective strain between 6 and 11% with the average breaking strength of 15 ± 3 Nm(-1) (23 GPa). The strength of strongest monolayer membranes is 11% of its Young's modulus, corresponding to the upper theoretical limit which indicates that the material can be highly crystalline and almost defect-free. Our results show that monolayer MoS(2) could be suitable for a variety of applications such as reinforcing elements in composites and for fabrication of flexible electronic devices.

Related Papers

• → Monolayer Behavior of Cyclic and Linear Forms of Surfactins: Thermodynamic Analysis of Langmuir Monolayers and AFM Study of Langmuir-Blodgett Monolayers(2014)13 cited
• → Stabilization of Langmuir monolayer of hydrophobic thiocholesterol molecules(2008)8 cited
• → On the characteristics of mixed Langmuir monolayer templates containing dipalmitoyl phosphatidylcholine for gold nanoparticle formation(2009)9 cited
• → On The Properties Of Surfactant Monolayers At Low Surface Tensions(2009)
• Metal-incorporated Langmuir Monolayers and Langmuir-Blodgett Films(2004)