One-Pot Synthesis of Intermetallic Electrocatalysts in Ordered, Large-Pore Mesoporous Carbon/Silica toward Formic Acid Oxidation
Citations Over TimeTop 10% of 2012 papers
Abstract
This study describes the one-pot synthesis and single-cell characterization of ordered, large-pore (>30 nm) mesoporous carbon/silica (OMCS) composites with well-dispersed intermetallic PtPb nanoparticles on pore wall surfaces as anode catalysts for direct formic acid fuel cells (DFAFCs). Lab-synthesized amphiphilic diblock copolymers coassemble hydrophobic metal precursors as well as hydrophilic carbon and silica precursors. The final materials have a two-dimensional hexagonal-type structure. Uniform and large pores, in which intermetallic PtPb nanocrystals are significantly smaller than the pore size and highly dispersed, enable pore backfilling with ionomers and formation of the desired triple-phase boundary in single cells. The materials show more than 10 times higher mass activity and significantly lower onset potential for formic acid oxidation as compared with commercial Pt/C, as well as high stability due to better resistivity toward CO poisoning. In single cells, the maximum power density was higher than that of commercial Pt/C, and the stability highly improved, compared with commercial Pd/C. The results suggest that PtPb-based catalysts on large-pore OMCSs may be practically applied as real fuel cell catalysts for DFAFC.
Related Papers
- → Activation energies of intermetallic compound growth at interface between Sn–5Bi–3.5Ag solder and Cu substrate(2003)12 cited
- → Effect of minor addition of Pb upon interfacial reactions and mechanical properties at Sn-3.0Ag-0.5Cu/Cu and Sn-58Bi/Cu solder joints(2008)4 cited
- → Alloys Based on Intermetallic Compounds(2021)2 cited
- → 14 Intermetallic materials(2005)2 cited
- → Fabrication and Microstructure of Fe-Al Intermetallic Compound Powders by Mechanical Alloying(2010)