Flexible and Transparent Dielectric Film with a High Dielectric Constant Using Chemical Vapor Deposition-Grown Graphene Interlayer

Citations Over TimeTop 10% of 2013 papers

Abstract

We have devised a dielectric film with a chemical vapor deposited graphene interlayer and studied the effect of the graphene interlayer on the dielectric performance. The highly transparent and flexible film was a polymer/graphene/polymer 'sandwich-structure' fabricated by a one-step transfer method that had a dielectric constant of 51, with a dielectric loss of 0.05 at 1 kHz. The graphene interlayer in the film forms a space charge layer, i.e., an accumulation of polarized charge carriers near the graphene, resulting in an induced space charge polarization and enhanced dielectric constant. The characteristic of the space charge layer for the graphene dielectric film, the sheet resistance of the graphene interlayer, was adjusted through thermal annealing that caused partial oxidation. The dielectric film with higher sheet resistance due to the oxidized graphene interlayer had a significantly lower dielectric constant compared to that with the graphene with lower interlayer sheet resistance. Oxidizing the graphene interlayer yields a smaller and thinner space charge density in the dielectric film, ultimately leading to decreased capacitance. Considering the simplicity of the fabrication process and high dielectric performance, as well as the high transparency and flexibility, this film is promising for applications in plastic electronics.

Related Papers

• → The effect of substrates on the Raman spectrum of graphene: Graphene- on-sapphire and graphene-on-glass(2007)250 cited
• → Orthotropic friction at the edges and interior of graphene and graphene fluoride and frictional anisotropy of graphene at the nanoscale(2021)1 cited
• A natural advantage? Using mined graphite to make graphene(2013)
• Synthesis and Characterisation of Graphene Single Sheets(2012)
• Unique synthesis of graphene-based materials for clean energy and biological sensing applications(2012)