Electrical Transport and Grain Growth in Solution-Cast, Chloride-Terminated Cadmium Selenide Nanocrystal Thin Films

Citations Over TimeTop 10% of 2014 papers

Abstract

We report the evolution of electrical transport and grain size during the sintering of thin films spin-cast from soluble phosphine and amine-bound, chloride-terminated cadmium selenide nanocrystals. Sintering of the nanocrystals occurs in three distinct stages as the annealing temperature is increased: (1) reversible desorption of the organic ligands (≤150 °C), (2) irreversible particle fusion (200-300 °C), and (3) ripening of the grains to >5 nm domains (>200 °C). Grain growth occurs at 200 °C in films with 8 atom % Cl(-), while films with 3 atom % Cl(-) resist growth until 300 °C. Fused nanocrystalline thin films (grain size = 4.5-5.5 nm) on thermally grown silicon dioxide gate dielectrics produce field-effect transistors with electron mobilities as high as 25 cm(2)/(Vs) and on/off ratios of 10(5) with less than 0.5 V hysteresis in threshold voltage without the addition of indium.

Related Papers

• → A single-electron transistor made from a cadmium selenide nanocrystal(1997)1,215 cited
• → A one-step synthesis of cadmium selenide quantum dots from a novel single source precursor(2003)91 cited
• → Synthesis of metal selenide colloidal nanocrystals by the hot injection of selenium powder(2013)18 cited
• → Tarnished thin film photoelectrodes — cadmium selenide(1983)6 cited
• → Kinetic Controlled-Growth Synthesis of Cadmium Selenide Nanocrystal Quantum Dots(2022)