Enhanced Sodium-Ion Battery Performance by Structural Phase Transition from Two-Dimensional Hexagonal-SnS2 to Orthorhombic-SnS
Citations Over TimeTop 1% of 2014 papers
Abstract
Structural phase transitions can be used to alter the properties of a material without adding any additional elements and are therefore of significant technological value. It was found that the hexagonal-SnS2 phase can be transformed into the orthorhombic-SnS phase after an annealing step in an argon atmosphere, and the thus transformed SnS shows enhanced sodium-ion storage performance over that of the SnS2, which is attributed to its structural advantages. Here, we provide the first report on a SnS@graphene architecture for application as a sodium-ion battery anode, which is built from two-dimensional SnS and graphene nanosheets as complementary building blocks. The as-prepared SnS@graphene hybrid nanostructured composite delivers an excellent specific capacity of 940 mAh g(-1)and impressive rate capability of 492 and 308 mAh g(-1) after 250 cycles at the current densities of 810 and 7290 mA g(-1), respectively. The performance was found to be much better than those of most reported anode materials for Na-ion batteries. On the basis of combined ex situ Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, and ex situ X-ray diffraction, the formation mechanism of SnS@graphene and the synergistic Na-storage reactions of SnS in the anode are discussed in detail. The SnS experienced a two-structural-phase transformation mechanism (orthorhombic-SnS to cubic-Sn to orthorhombic-Na3.75Sn), while the SnS2 experienced a three-structural-phase transformation mechanism (hexagonal-SnS2 to tetragonal-Sn to orthorhombic-Na3.75Sn) during the sodiation process. The lesser structural changes of SnS during the conversion are expected to lead to good structural stability and excellent cycling stability in its sodium-ion battery performance. These results demonstrate that the SnS@graphene architecture offers unique characteristics suitable for high-performance energy storage application.
Related Papers
- → Orthorhombic-to-Hexagonal Phase Transition of REF3 (RE = Sm to Lu and Y) under High Pressure(2022)9 cited
- → Cyclic Phase Transition from Hexagonal to Orthorhombic Then Back to Hexagonal of EuF3 While Loading Uniaxial Pressure and under High Temperature(2016)12 cited
- A natural advantage? Using mined graphite to make graphene(2013)
- Unique synthesis of graphene-based materials for clean energy and biological sensing applications(2012)
- → Orthotropic friction at the edges and interior of graphene and graphene fluoride and frictional anisotropy of graphene at the nanoscale(2021)