Sub-3 nm Co3O4 Nanofilms with Enhanced Supercapacitor Properties
Citations Over TimeTop 1% of 2015 papers
Abstract
Two-dimensional materials often show a range of intriguing electronic, catalytic, and optical properties that differ greatly from conventional nanoparticles. Herein, we demonstrate the large-scale preparation of sub-3 nm atomic layers Co3O4 nanofilms with a nonsurfactant and substrate-free hydrothermal method. This successful preparation of ultrathin nanofilms highlighted the reconstruction of cobalt-ammonia complexes and synergistic effect of free ammonia and nitrate on film growth control. Subsequent performance tests uncovered that these sub-3 nm atomic layer Co3O4 nanofilms exhibited an ultrahigh specific capacitance of 1400 F/g in the first galvanostatic charge/discharge test. The specific capacitance of Co3O4 nanofilms only slightly decayed less than 3% after 1500 cycling tests. With some parameter adjustments, similar Co(OH)2 nanofilms with a thickness of 3.70 ± 0.10 nm were also prepared. The Co(OH)2 nanofilms possessed maximum specific capacitance of 1076 F/g and peak performance attenuation of about 2% after a cycle stability test.
Related Papers
- → Asymmetric supercapacitors based on high capacitance Ni6MnO8 and graphene(2019)24 cited
- → A Revisit to Supercapacitor Capacitance Measurement Method 1A of IEC 62391-1(2018)19 cited
- → Extrinsic design of high-performance programmable supercapacitor with large specific areal capacitance(2023)15 cited
- → Graphene based Supercapacitors with Improved Specific Capacitance and Fast Charging Time at High Current Density(2013)32 cited
- → Synthesis of NiCo2S4@NiMoO4 Nanosheets with Excellent Electrochemical Performance for Supercapacitor(2021)1 cited