Fluorescence and Spin Properties of Defects in Single Digit Nanodiamonds

Citations Over TimeTop 1% of 2009 papers

Abstract

This article reports stable photoluminescence and high-contrast optically detected electron spin resonance (ODESR) from single nitrogen-vacancy (NV) defect centers created within ultrasmall, disperse nanodiamonds of radius less than 4 nm. Unexpectedly, the efficiency for the production of NV fluorescent defects by electron irradiation is found to be independent of the size of the nanocrystals. Fluorescence lifetime imaging shows lifetimes with a mean value of around 17 ns, only slightly longer than the bulk value of the defects. After proper surface cleaning, the dephasing times of the electron spin resonance in the nanocrystals approach values of some microseconds, which is typical for the type Ib diamond from which the nanoparticle is made. We conclude that despite the tiny size of these nanodiamonds the photoactive nitrogen-vacancy color centers retain their bulk properties to the benefit of numerous exciting potential applications in photonics, biomedical labeling, and imaging.

Related Papers

• → Nanoscale magnetometry through quantum control of nitrogen–vacancy centres in rotationally diffusing nanodiamonds(2013)33 cited
• → Bioimaging and Quantum Sensing Using NV Centers in Diamond Nanoparticles(2016)6 cited
• → Nanodiamonds: Nanodiamonds That Swim (Adv. Mater. 30/2017)(2017)3 cited
• → Photoluminescence Enhancement from a Single Nitrogen Vacancy Center in a Nanodiamond Crystal via a Metal Nanoantenna(2013)2 cited
• → Fluorescence profile of a nitrogen-vacancy center in a nanodiamond(2022)