Discrete plasticity in sub-10-nm-sized gold crystals

Citations Over TimeTop 10% of 2010 papers

Abstract

Although deformation processes in submicron-sized metallic crystals are well documented, the direct observation of deformation mechanisms in crystals with dimensions below the sub-10-nm range is currently lacking. Here, through in situ high-resolution transmission electron microscopy (HRTEM) observations, we show that (1) in sharp contrast to what happens in bulk materials, in which plasticity is mediated by dislocation emission from Frank-Read sources and multiplication, partial dislocations emitted from free surfaces dominate the deformation of gold (Au) nanocrystals; (2) the crystallographic orientation (Schmid factor) is not the only factor in determining the deformation mechanism of nanometre-sized Au; and (3) the Au nanocrystal exhibits a phase transformation from a face-centered cubic to a body-centered tetragonal structure after failure. These findings provide direct experimental evidence for the vast amount of theoretical modelling on the deformation mechanisms of nanomaterials that have appeared in recent years.

Related Papers

• → Motion of 1/3⟨111⟩ dislocations on Σ3 {112} twin boundaries in nanotwinned copper(2014)25 cited
• → High-Resolution Transmission Electron Microscopy (HRTEM) in the Study of Clays and Soils(1990)7 cited
• → Structures of dissociated 〈11¯00〉 dislocations and {11¯00} stacking faults of alumina (α-Al2O3)(2009)28 cited
• → Cross-sectional HRTEM study of Si(5 5 12) reconstructed surface(2002)23 cited
• → 10.1063/1.4861868.1(2014)