One hundred fold increase in current carrying capacity in a carbon nanotube–copper composite
Citations Over TimeTop 1% of 2013 papers
Abstract
Increased portability, versatility and ubiquity of electronics devices are a result of their progressive miniaturization, requiring current flow through narrow channels. Present-day devices operate close to the maximum current-carrying-capacity (that is, ampacity) of conductors (such as copper and gold), leading to decreased lifetime and performance, creating demand for new conductors with higher ampacity. Ampacity represents the maximum current-carrying capacity of the object that depends both on the structure and material. Here we report a carbon nanotube-copper composite exhibiting similar conductivity (2.3-4.7 × 10(5) S cm(-1)) as copper (5.8 × 10(5) S cm(-1)), but with a 100-times higher ampacity (6 × 10(8) A cm(-2)). Vacuum experiments demonstrate that carbon nanotubes suppress the primary failure pathways in copper as observed by the increased copper diffusion activation energy (~2.0 eV) in carbon nanotube-copper composite, explaining its higher ampacity. This is the only material with both high conductivity and high ampacity, making it uniquely suited for applications in microscale electronics and inverters.
Related Papers
- → Miniaturization for the Development of High Performance Separation Systems(2017)17 cited
- → Analysis of Technical and Economic Characteristics of New Generation Conductors(2015)
- → Kissing of Sub-conductors due to Magnetic Forces in a 154 kV Bundled Overhead Transmission Line(2016)
- → Estimation of Magnetic Fields near to High Temperature Low Sag Conductors(2020)
- Miniaturization of Separation Systems and Its Applications(2003)