Rapid epitaxy-free graphene synthesis on silicidated polycrystalline platinum
Citations Over TimeTop 10% of 2015 papers
Abstract
Large-area synthesis of high-quality graphene by chemical vapour deposition on metallic substrates requires polishing or substrate grain enlargement followed by a lengthy growth period. Here we demonstrate a novel substrate processing method for facile synthesis of mm-sized, single-crystal graphene by coating polycrystalline platinum foils with a silicon-containing film. The film reacts with platinum on heating, resulting in the formation of a liquid platinum silicide layer that screens the platinum lattice and fills topographic defects. This reduces the dependence on the surface properties of the catalytic substrate, improving the crystallinity, uniformity and size of graphene domains. At elevated temperatures growth rates of more than an order of magnitude higher (120 μm min(-1)) than typically reported are achieved, allowing savings in costs for consumable materials, energy and time. This generic technique paves the way for using a whole new range of eutectic substrates for the large-area synthesis of 2D materials.
Related Papers
- → Electrochemistry of graphene, graphene oxide and other graphenoids: Review(2013)266 cited
- → Orthotropic friction at the edges and interior of graphene and graphene fluoride and frictional anisotropy of graphene at the nanoscale(2021)1 cited
- A natural advantage? Using mined graphite to make graphene(2013)
- Synthesis and Characterisation of Graphene Single Sheets(2012)
- Unique synthesis of graphene-based materials for clean energy and biological sensing applications(2012)