Fabrication of high-quality single-crystal Cu thin films using radio-frequency sputtering
Citations Over TimeTop 17% of 2014 papers
Abstract
Copper (Cu) thin films have been widely used as electrodes and interconnection wires in integrated electronic circuits, and more recently as substrates for the synthesis of graphene. However, the ultra-high vacuum processes required for high-quality Cu film fabrication, such as molecular beam epitaxy (MBE), restricts mass production with low cost. In this work, we demonstrated high-quality Cu thin films using a single-crystal Cu target and radio-frequency (RF) sputtering technique; the resulting film quality was comparable to that produced using MBE, even under unfavorable conditions for pure Cu film growth. The Cu thin film was epitaxially grown on an Al2O3 (sapphire) (0001) substrate, and had high crystalline orientation along the (111) direction. Despite the 10(-3) Pa vacuum conditions, the resulting thin film was oxygen free due to the high chemical stability of the sputtered specimen from a single-crystal target; moreover, the deposited film had >5× higher adhesion force than that produced using a polycrystalline target. This fabrication method enabled Cu films to be obtained using a simple, manufacturing-friendly process on a large-area substrate, making our findings relevant for industrial applications.
Related Papers
- → Plasma-assisted molecular-beam epitaxy of AlN(112¯2) on m sapphire(2007)60 cited
- → High-Temperature Heat-Treatment of c-, a-, r-, and m-Plane Sapphire Substrates in Mixed Gases of H2 and N2(2013)11 cited
- → Ion plasma sputtering of multi-component materials(1998)4 cited
- → Effects of radiation-induced segregation and preferential sputtering on the sputtering rate of alloys(1979)10 cited
- → Sputtering of Lunar Regolith by Solar Wind Protons and Heavy Ions, and General Aspects of Potential Sputtering(2014)