Fracture-induced amorphization of polycrystalline SiO2 stishovite: a potential platform for toughening in ceramics

Citations Over TimeTop 11% of 2014 papers

Abstract

Silicon dioxide has eight stable crystalline phases at conditions of the Earth's rocky parts. Many metastable phases including amorphous phases have been known, which indicates the presence of large kinetic barriers. As a consequence, some crystalline silica phases transform to amorphous phases by bypassing the liquid via two different pathways. Here we show a new pathway, a fracture-induced amorphization of stishovite that is a high-pressure polymorph. The amorphization accompanies a huge volume expansion of ~100% and occurs in a thin layer whose thickness from the fracture surface is several tens of nanometers. Amorphous silica materials that look like strings or worms were observed on the fracture surfaces. The amount of amorphous silica near the fracture surfaces is positively correlated with indentation fracture toughness. This result indicates that the fracture-induced amorphization causes toughening of stishovite polycrystals. The fracture-induced solid-state amorphization may provide a potential platform for toughening in ceramics.

Related Papers

• → An instrumented indentation technique for estimating fracture toughness of ductile materials: A critical indentation energy model based on continuum damage mechanics(2005)159 cited
• → Effect of loading conditions on the fracture toughness of zirconia(2013)55 cited
• → ISE and fracture toughness evaluation by Vickers hardness testing of an Al3Nb–Nb2Al–AlNbNi in situ composite(2008)33 cited
• → Fracture Toughness of Chemically Vapor‐Deposited Diamond(1991)51 cited
• → Evaluation of Fracture Toughness Using SENB Specimens with Precrack Produced by Growing Microcrack Around Vickers' Indent(1987)3 cited