Graphene-Co3O4 nanocomposite as electrocatalyst with high performance for oxygen evolution reaction

Citations Over TimeTop 1% of 2015 papers

Abstract

Graphene-Co3O4 composite with a unique sandwich-architecture was successfully synthesized and applied as an efficient electrocatalyst for oxygen evolution reaction. Field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM) analyses confirmed that Co3O4 nanocrystals were homogeneously distributed on both sides of graphene nanosheets. The obtained composite shows enhanced catalytic activities in both alkaline and neutral electrolytes. The onset potential towards the oxygen evolution reaction is 0.406 V (vs. Ag/AgCl) in 1 M KOH solution and 0.858 V (vs. Ag/AgCl) in neutral phosphate buffer solution (PBS), respectively. The current density of 10 mA/cm2 has been achieved at the overpotential of 313 mV in 1 M KOH and 498 mV in PBS. The graphene-Co3O4 composite also exhibited an excellent stability in both alkaline and neutral electrolytes. In particular, no obvious current density decay was observed after 10 hours testing in alkaline solution and the morphology of the material was well maintained, which could be ascribed to the synergistic effect of combining Co3O4 and graphene.

Related Papers

• → Thermo-selenizing to rationally tune surface composition and evolve structure of stainless steel to electrocatalytically boost oxygen evolution reaction(2020)59 cited
• → Facile synthesis of interlaced flower-like layered double hydroxides grown on porous CoMoP as a highly efficient electrocatalyst for hydrogen evolution reaction(2023)33 cited
• → Oxygen Evolution Reaction (OER) on Clean and Oxygen Deficient Low-Index SrTiO₃ Surfaces: A Theoretical Systematic Study(2019)20 cited
• → Cover Picture: A 3D Nanoporous Ni–Mo Electrocatalyst with Negligible Overpotential for Alkaline Hydrogen Evolution (ChemElectroChem 7/2014)(2014)4 cited
• → A 3D Nanoporous Ni–Mo Electrocatalyst with Negligible Overpotential for Alkaline Hydrogen Evolution(2014)4 cited