Synthesis of Large-Area WS2 monolayers with Exceptional Photoluminescence

Citations Over TimeTop 1% of 2016 papers

Abstract

Monolayer WS2 offers great promise for use in optical devices due to its direct bandgap and high photoluminescence intensity. While fundamental investigations can be performed on exfoliated material, large-area and high quality materials are essential for implementation of technological applications. In this work, we synthesize monolayer WS2 under various controlled conditions and characterize the films using photoluminescence, Raman and x-ray photoelectron spectroscopies. We demonstrate that the introduction of hydrogen to the argon carrier gas dramatically improves the optical quality and increases the growth area of WS2, resulting in films exhibiting mm(2) coverage. The addition of hydrogen more effectively reduces the WO3 precursor and protects against oxidative etching of the synthesized monolayers. The stoichiometric WS2 monolayers synthesized using Ar + H2 carrier gas exhibit superior optical characteristics, with photoluminescence emission full width half maximum (FWHM) values below 40 meV and emission intensities nearly an order of magnitude higher than films synthesized in a pure Ar environment.

Related Papers

• → La2MgTiO6:Bi3+/Mn4+ photoluminescence materials: Molten salt preparation, Bi3+ → Mn4+ energy transfer and thermostability(2020)21 cited
• → Photoluminescence of porous Si, oxidized then deoxidized chemically(1992)109 cited
• → Stabilization of Langmuir monolayer of hydrophobic thiocholesterol molecules(2008)8 cited
• → Study of delocalized and localized states in ZnSeO layers with photoluminescence, micro-photoluminescence, and time-resolved photoluminescence(2019)7 cited
• → Ballistic effect and new concept of Si wire photoluminescence(2003)1 cited