A Novel Approach Toward Fabrication of High Performance Thin Film Composite Polyamide Membranes
Citations Over TimeTop 1% of 2016 papers
Abstract
A practical method is reported to enhance water permeability of thin film composite (TFC) polyamide (PA) membranes by decreasing the thickness of the selective PA layer. The composite membranes were prepared by interfacial polymerization (IP) reaction between meta-phenylene diamine (MPD)-aqueous and trimesoyl chloride (TMC)-organic solvents at the surface of polyethersulfone (PES) microporous support. Several PA TFC membranes were prepared at different temperatures of the organic solution ranging from -20 °C to 50 °C. The physico-chemical and morphological properties of the synthesized membranes were carefully characterized using serval analytical techniques. The results confirmed that the TFC membranes, synthesized at sub-zero temperatures of organic solution, had thinner and smoother PA layer with a greater degree of cross-linking and wettability compared to the PA films prepared at 50 °C. We demonstrated that reducing the temperature of organic solution effectively decreased the thickness of the PA active layer and thus enhanced water permeation through the membranes. The most water permeable membrane was prepared at -20 °C and exhibited nine times higher water flux compared to the membrane synthesized at room temperature. The method proposed in this report can be effectively applied for energy- and cost-efficient development of high performance nanofiltration and reverse osmosis membranes.
Related Papers
- → Regulating the interfacial polymerization process toward high-performance polyamide thin-film composite reverse osmosis and nanofiltration membranes: A review(2021)261 cited
- → Truly chlorine-resistant polyamide reverse osmosis composite membrane(1996)10 cited
- Interfacially synthesized thin-film composite reverse osmosis membranes and their surface modification(2011)
- Progress on thin-film composite(TFC)reverse osmosis membrane(2013)
- → Truly chlorine‐resistant polyamide reverse osmosis composite membrane(1996)