Multi-Functional Carbon Fibre Composites using Carbon Nanotubes as an Alternative to Polymer Sizing
Citations Over TimeTop 1% of 2016 papers
Abstract
Carbon fibre reinforced polymers (CFRP) were introduced to the aerospace, automobile and civil engineering industries for their high strength and low weight. A key feature of CFRP is the polymer sizing - a coating applied to the surface of the carbon fibres to assist handling, improve the interfacial adhesion between fibre and polymer matrix and allow this matrix to wet-out the carbon fibres. In this paper, we introduce an alternative material to the polymer sizing, namely carbon nanotubes (CNTs) on the carbon fibres, which in addition imparts electrical and thermal functionality. High quality CNTs are grown at a high density as a result of a 35 nm aluminium interlayer which has previously been shown to minimise diffusion of the catalyst in the carbon fibre substrate. A CNT modified-CFRP show 300%, 450% and 230% improvements in the electrical conductivity on the 'surface', 'through-thickness' and 'volume' directions, respectively. Furthermore, through-thickness thermal conductivity calculations reveal a 107% increase. These improvements suggest the potential of a direct replacement for lightning strike solutions and to enhance the efficiency of current de-icing solutions employed in the aerospace industry.
Related Papers
- → Semi-dry Sizing(1966)
- Research on the function of drawing roller in sizing machine(2006)
- A discussion about sizing high-polyester and cotton fabric without PVA(2012)
- The production and application of a new integrated surface sizing modifier(2006)
- The application of S432 sizing machine in special fine yarn sizing(2007)