Influence of pH and ionic strength on vanadium(v) oxides formation. From V2O5·nH2O gels to crystalline NaV3O8·1.5H2O
Citations Over TimeTop 10% of 2005 papers
Abstract
Na+ and TMA+ intercalated M0.3V2O5·1.5H2O (M = Na+ and TMA+) precipitates have been synthesized by adding chloride salts MCl or bases MOH to a metavanadate solution which was acidified using a proton exchange resin. As evidenced by X-ray diffraction, these vanadium oxides exhibit the layered structure of the V2O5·1.8H2O xerogels in which Na+ and TMA+ cations are intercalated between the layers. These precipitates result from the assembly of ribbon-like particles but in contrast to the V2O5·1.8H2O xerogels, the particles are no longer stacked on flat surfaces and their assembly is disorganized as evidenced by SEM and TEM. Depending on the final pH of the acidified metavanadate solution, the Na0.3V2O5·1.5H2O phase can be thermodynamically stable or can evolve with time. At a pH > 3, the Na0.3V2O5·1.5H2O phase disappears after a few days and is transformed to the crystalline NaV3O8·1.5H2O phase. The vanadium oxide phases were all characterized by X-ray diffraction, SEM, TEM, TGA, IR and 51V MAS NMR.
Related Papers
- → Magnéli phase vanadium oxide thin films produced by stepwise oxidation of vanadium metal foil(2022)4 cited
- → Spectroscopic characterization of vanadium(V) oxo species deposited on zirconia(2000)15 cited
- STUDY ON EXCHANGING PROPERTIES OF ANION EXCHANGE RESINS FOR VANADIUM (V)(2002)
- Comparative study on Al_2O_3 or SiO_2 supported vanadium oxides by UV-Raman spectrometry(2008)
- → Effects of Vanadate Solution Property on the Precipitation of Ammonium (Meta, Poly)Vanadate(2023)