Shell and ligand-dependent blinking of CdSe-based core/shell nanocrystals

Citations Over TimeTop 16% of 2010 papers

Abstract

Blinking of zinc blende CdSe-based core/shell nanocrystals is studied as a function of shell materials and surface ligands. CdSe/ZnS, CdSe/ZnSe/ZnS and CdSe/CdS/ZnS core/shell nanocrystals are prepared by colloidal synthesis and six monolayers of larger bandgap shell materials are grown over the CdSe core. Organic-soluble nanocrystals covered with stearate are made water-soluble by ligand exchange with 3-mercaptopropionic acid. The light-emitting states of nanocrystals are characterized by absorption and emission spectroscopy as well as photoluminescence lifetime measurements in solution. The blinking time trace is recorded for single nanocrystals on a glass coverslip. Both on- and off-time distributions are fitted to the power law. The power-law exponents vary, depending on shell materials and surface ligands. The off-time exponents for organic and water-soluble nanocrystals are measured in the range of 1.36-1.55 and 1.25-1.37, respectively, while their on-time exponents are spread in the range of 1.53-1.86 and 1.85-2.17, respectively. Water-soluble surface passivation with thiolate prolongs the dark period regardless of shell materials and core/shell structures. Of the core/shell structures, CdSe/CdS/ZnS exhibits the longest bright state. The on/off-time exponents are inversely correlated, although the successive on/off events are not individually correlated. A two competing charge-tunneling model is presented to describe the variation of on- and off-time exponents with shell materials and surface ligands.

Related Papers

• → Elimination of parasitic effects in floating junction rear surface passivation for solar cells(1996)17 cited
• → Sulfur passivation of 3C-SiC thin film(2018)4 cited
• → A new method for bulk passivation in multicrystalline-Si by sulfur(2015)2 cited
• Development of High Performance Chromium-Free Passivation Agent Suitable for Coating of Aluminum Alloy and Optimization of Passivation Technology(2012)
• Passivation method of 317L stainless steel used in medicine(2002)