Surface strontium enrichment on highly active perovskites for oxygen electrocatalysis in solid oxide fuel cells

Citations Over TimeTop 1% of 2012 papers

Abstract

Perovskite oxides have high catalytic activities for oxygen electrocatalysis competitive to platinum at elevated temperatures. However, little is known about the oxide surface chemistry that influences the activity near ambient oxygen partial pressures, which hampers the design of highly active catalysts for many clean-energy technologies such as solid oxide fuel cells. Using in situsynchrotron-based, ambient pressure X-ray photoelectron spectroscopy to study the surface chemistry changes, we show that the coverage of surface secondary phases on a (001)-oriented La0.8Sr0.2CoO3−δ (LSC) film becomes smaller than that on an LSC powder pellet at elevated temperatures. In addition, strontium (Sr) in the perovskite structure enriches towards the film surface in contrast to the pellet having no detectable changes with increasing temperature. We propose that the ability to reduce surface secondary phases and develop Sr-enriched perovskite surfaces of the LSC film contributes to its enhanced activity for O2 electrocatalysis relative to LSC powder-based electrodes.

Related Papers

• → Nitrogen-modified metal-organic framework-based carbon: An effective non-precious electrocatalyst for oxygen reduction reaction(2020)17 cited
• → A high performance non-noble metal electrocatalyst for the oxygen reduction reaction derived from a metal organic framework(2016)21 cited
• → Aims of Electrocatalysis(2015)1 cited
• Preparation and characterization of La_(0.6) Ca_(0.4) CoO_3 as bifunctional oxygen electrode electrocatalyst(2004)
• On physico-chemical aspects of electrocatalysis(1986)