Photoanodic behavior of vapor-liquid-solid–grown, lightly doped, crystalline Si microwire arrays
Citations Over TimeTop 10% of 2012 papers
Abstract
Arrays of n-Si microwires have to date exhibited low efficiencies when measured as photoanodes in contact with a 1-1′-dimethylferrocene (Me2Fc+/0)–CH3OH solution. Using high-purity Au or Cu catalysts, arrays of crystalline Si microwires were grown by a vapor-liquid-solid process without dopants, which produced wires with electronically active dopant concentrations of 1 × 1013 cm−3. When measured as photoanodes in contact with a Me2Fc+/0–CH3OH solution, the lightly doped Si microwire arrays exhibited greatly increased fill factors and efficiencies as compared to n-Si microwires grown previously with a lower purity Au catalyst. In particular, the Cu-catalyzed Si microwire array photoanodes exhibited open-circuit voltages of ∼0.44 V, carrier-collection efficiencies exceeding ∼0.75, and an energy-conversion efficiency of 1.4% under simulated air mass 1.5 G illumination. Lightly doped Cu-catalyzed Si microwire array photoanodes have thus demonstrated performance that is comparable to that of optimally doped p-type Si microwire array photocathodes in photoelectrochemical cells.
Related Papers
- → Advances in Light-Emitting Doped Semiconductor Nanocrystals(2011)256 cited
- → Effect of ZrO2 doping on the tunable and dielectric properties of Ba0.55Sr0.45TiO3/MgO composites for microwave tunable application(2006)15 cited
- → The Effect of Sn/Si Dopant on Optical and Structural Properties of Nanostructured Zinc Oxide Thin Films(2016)4 cited
- → Modelling the concentration dependence of doping in optical materials(2015)
- → The role of surface stoichiometry in the activity of doped vanadia-based catalysts for the selective catalytic reduction(2022)