Lithium storage in nitrogen-rich mesoporous carbon materials
Citations Over TimeTop 1% of 2012 papers
Abstract
Nitrogen-rich mesoporous carbon materials were obtained by pyrolyzing gelatin between 700 and 900 °C with a nano-CaCO3 template. The mesoporous structure and the high nitrogen content endowed these materials with reversible capacities up to ca. 1200 mA h g−1. The high specific surface area and the nitrogen doping are responsible for the capacity loss in the initial cycle. FTIR and XPS studies indicate that the nitrogen in the material exists in the form of pyridinic, pyrrolic/pyridonic and graphitic nitrogen. The Raman spectroscopic analysis indicates that the structure of the mesoporous carbon becomes more disordered during discharge and is restored during recharge, a behavior similar to that in nitrogen-free hard carbon materials. The reversible structural variation of these carbon materials ensures their high cyclic reversibility.
Related Papers
- → Unraveling Ce3+ detection at the surface of ceria nanopowders by UPS analysis(2022)24 cited
- → Ambient-Pressure X-ray Photoelectron Spectroscopy (APXPS)(2016)26 cited
- → Chemical Analysis of Ionic Liquids Using Photoelectron Spectroscopy(2016)19 cited
- → Chapter 12.4 X-ray Photoelectron Spectroscopy(2006)14 cited
- → The effect of aqueous solution in Raman spectroscopy(2009)3 cited