Facile synthesis of Fe-containing metal–organic frameworks as highly efficient catalysts for degradation of phenol at neutral pH and ambient temperature
Citations Over TimeTop 21% of 2015 papers
Abstract
In this work, MIL-53(Fe) was synthesized using a solvothermal method under static conditions. However, it was interesting to find that another MIL-53 type material, Fe(BDC)(DMF,F), was obtained when stirring conditions were used while keeping the other conditions fixed. The Fe-containing metal–organic frameworks (MOFs) were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), 57Fe Mössbauer spectrometry and thermogravimetric analysis (TGA). By simply increasing the crystallization time under agitation, the morphology of the Fe(BDC)(DMF,F) crystals went through a striking transition from a bulky irregular shape to a rod-like morphology. The catalytic performance of the Fe-MOFs was evaluated in the degradation of phenol solution at near neutral pH at 35 °C. A significantly better catalytic activity was achieved for Fe(BDC)(DMF,F) than for MIL-53(Fe) and NH2-MIL-53(Fe) due to the existence of Fe(II) in its framework. Phenol was almost completely decomposed in 3 hours, and the conversions of hydrogen peroxide and chemical oxygen demand (COD) were 74.1% and 78.7%, respectively.
Related Papers
- → The thermogravimetric analysis of some polysiloxanes(1998)186 cited
- → The use of thermogravimetric analysis technique for the characterization of construction materials(2008)77 cited
- → Kinetic analysis of thermogravimetric data on some nickel(II) N-alkyldithiocarbamates(1989)25 cited
- → Thermogravimetric analysis for the characterization and comparative analysis of polyvinyl chloride (PVC) wall panel(2023)1 cited
- Thermogravimetric analysis of fuel film evaporation(2006)