Discrimination between two memory channels by molecular alloying in a doubly bistable spin crossover material

Citations Over TimeTop 12% of 2019 papers

Abstract

A multistable spin crossover (SCO) molecular alloy system [Fe_1-x M _x (nBu-im)₃(tren)](P_1-y As _y F₆)₂ (M = ZnII, NiII; (nBu-im)₃(tren) = tris(n-butyl-imidazol(2-ethylamino))amine) has been synthesized and characterized. By controlling the composition of this isomorphous series, two cooperative thermally induced SCO events featuring distinct critical temperatures (T _c) and hysteresis widths (ΔT _c, memory) can be selected at will. The pristine derivative 100As (x = 0, y = 1) displays a strong cooperative two-step SCO and two reversible structural phase transitions (PTs). The low temperature PTLT and the SCO occur synchronously involving conformational changes of the ligand's n-butyl arms and two different arrangements of the AsF₆ - anions [T1c = 174 K (ΔT1c = 17 K), T2c = 191 K (ΔT2c = 23 K) (scan rate 2 K min-1)]. The high-temperature PTHT takes place in the high-spin state domain and essentially involves rearrangement of the AsF₆ - anions [TPTc = 275 K (ΔTPTc = 16 K)]. This behavior strongly contrasts with that of the homologous 100P [x = 0, y = 0] derivative where two separate cooperative one-step SCO can be selected by controlling the kinetics of the coupled PTLT at ambient pressure: (i) one at low temperatures, T _c = 122 K (ΔT _c = 9 K), for temperature scan rates (>1 K min-1) (memory channel A) where the structural modifications associated with PTLS are inhibited; (ii) the other centered at T _c = 155 K (ΔT _c = 41 K) for slower temperature scan rates ≤0.1 K min-1 (memory channel B). These two SCO regimes of the 100P derivative transform reversibly into the two-step SCO of 100As upon application of hydrostatic pressure (ca. 0.1 GPa) denoting the subtle effect of internal chemical pressure on the SCO behavior. Precise control of AsF₆ - ↔ PF₆ - substitution, and hence of the PTLT kinetics, selectively selects the memory channel B of 100P when x = 0 and y ≈ 0.7. Meanwhile, substitution of FeII with ZnII or NiII [x ≈ 0.2, y = 0] favors the low temperature memory channel A at any scan rate. This intriguing interplay between PT, SCO and isomorphous substitution was monitored by single crystal and powder X-ray diffractometries, and magnetic and calorimetric measurements.

Related Papers

• → Design of Deployable Structures by Using Bistable Compliant Mechanisms(2022)38 cited
• → Dynamic bistable switches enhance robustness and accuracy of cell cycle transitions(2021)36 cited
• → Loss and recovery of bistability of organic bistable devices(2009)10 cited
• → Bistable criterion for mechanically bistable mechanism(2012)7 cited
• → Origami-Based Rotating Bistable Mechanism(2023)1 cited