The effect of pit size and density on the fatigue behaviour of a pre‐corroded martensitic stainless steel

Citations Over TimeTop 21% of 2018 papers

Abstract

Abstract UNS S17400 steel is used in turbines for the aerospace and utility industries. While it is generally corrosion resistant, it is susceptible to pitting when exposed to aqueous chloride environments. Effects of pitting characteristics, such as depth, width, and local density on fatigue life, have been studied in this work to better inform criteria for component replacement or repair. While pit depth correlates well with cracking, the deepest pit never initiated the crack that ultimately led to failure. The clustering of pits, or local pitting density, also correlated well with crack initiation location; however, the densest region of pitting was not always the location where cracking occurred. There is likely no single metric that directly correlates pitting with fatigue cracking, rather there is a combination of pitting characteristics that ultimately lead to cracking. The results from this work suggest that pit depth and local pitting density are among the more important metrics.

Related Papers

• → Initial Stage of Pitting Corrosion of Type 304 Stainless Steel under Thin Electrolyte Layers Containing Chloride Ions(2005)64 cited
• → Influence of temperature on the pitting corrosion behavior of AISI 316L in chloride–CO2 (sat.) solutions(2014)28 cited
• → Pitting Corrosion of Type 430 Stainless Steel in the Process of Drying of Chloride Solution Layer(2012)9 cited
• Influence of loading cracking on chloride ions diffusion in concrete(2011)
• Study on the chloride ion concentration threshold value of the pitting corrosion of 304 stainless steel in circulating cooling water(2012)