A Composite Electrode Based on Graphite and β-Li[sub 3]N for Li-Ion Batteries

Citations Over Time

Abstract

In this paper the electrochemical characterization of a composite electrode based on β-lithium nitride iron, and synthetic graphite is reported. the high pressure form of was obtained by ballmilling a mixture of and iron metal. The electrochemical behavior of mixtures and pure graphite electrodes was also studied. It was found that lithium can be extracted from the in the presence of iron at a flat potential of 1.1 V vs. Li. A specific capacity as high as was recorded during the first lithium extraction. A drastic reduction of the capacity was observed on further cycling. The was used as a source of lithium for the lithiation of graphite composite electrodes. A composite electrode was prepared assuming that all the lithium extracted from was reinserted into the graphite during cycling. Upon cycling, a progressive decrease in the contribution to the electrode capacity and, concurrently, an increase in the graphite contribution were observed and after 320 cycles lithium was intercalated exclusively into the graphite. The electrode cycled for 500 cycles with a specific capacity of (based on the graphite weight) without any capacity loss. © 2003 The Electrochemical Society. All rights reserved.

Related Papers

• → Simulation of Atomic-Scale Ultralow Friction of Graphite/C₆₀/Graphite Interface along [1010] Direction(2007)24 cited
• → Classification of degenerate graphite and its formation processes in heavy section ductile iron(1989)20 cited
• → Preparation of Graphite Single-Crystal from an Iron Solution by a Temperature-Gradient Method(1990)2 cited
• → Effect of Expansion Temperature of Expandable Graphite on Anti-Friction Effect of Graphite Nonasheets from Sonicating Expanded Graphite(2011)
• Study on graphite/NR thermal conductive composite(2010)