Organic Solar Cells with Boron- or Nitrogen-Doped Carbon Nanotubes in the P3HT : PCBM Photoactive Layer
Citations Over TimeTop 23% of 2016 papers
Abstract
Either boron- or nitrogen-doped carbon nanotubes (B- or N-CNTs) were incorporated in bulk heterojunction organic solar cells photoactive layer composed of poly(3-hexylthiophene) (P3HT) : (6,6)-phenyl-C 61 -butyric acid methyl ester (PCBM). The physical and chemical properties were investigated using different spectroscopic techniques. The cell performance was followed from their current-voltage (J-V) characteristics. Recombination dynamics of the photo-generated free charge carriers were investigated using micro- to milliseconds transient absorption spectroscopy (TAS). Transmission electron microscopy (TEM) images revealed the presence of cone structures and bamboo compartments in B-CNTs and N-CNTs, respectively. X-ray photoelectron spectroscopy (XPS) revealed very little boron was substituted in the carbon network and presence of pyrrolic, pyridinic, and quaternary species of nitrogen in N-CNTs.J-Vcharacteristics were found to be similar for the devices with B- and N-CNTs even though boron- and nitrogen-doped CNTs are known to have different properties, that is, p-type and n-type, respectively. TAS results showed that all devices had long lived free charge carriers but the devices with B- or N-CNTs had low power conservation efficiency and voltage.
Related Papers
- → Ambient-Pressure X-ray Photoelectron Spectroscopy (APXPS)(2016)26 cited
- → Chemical Analysis of Ionic Liquids Using Photoelectron Spectroscopy(2016)19 cited
- → Chapter 12.4 X-ray Photoelectron Spectroscopy(2006)14 cited
- → Analysis of Chemical Composition of Biopolymers and Biomaterials: An XPS Study(2023)1 cited
- → Introduction to XPS Analysis for Beginners(2019)