Age-related changes in the tensile properties of cortical bone. The relative importance of changes in porosity, mineralization, and microstructure.

Citations Over TimeTop 10% of 1993 papers

Abstract

Tensile testing to failure was done on 235 cortical specimens that had been machined from forty-seven femora from human cadavera. The donors had ranged in age from twenty to 102 years at the time of death. After mechanical testing, the porosity, mineralization, and microstructure were determined. Linear regression analysis showed that the mechanical properties deteriorated markedly with age. Ultimate stress, ultimate strain, and energy absorption decreased by 5, 9, and 12 per cent per decade, respectively. The porosity of bone increased significantly with age, while the mineral content was not affected. Microstructural analysis demonstrated that the amount of haversian bone increased with age. Both bivariate and multivariate analyses demonstrated the importance of age-related changes in porosity to the decline in mechanical properties. Changes in porosity accounted for 76 per cent of the reduction in strength. Microstructural changes were highly correlated with porosity and therefore had little independent effect. Mineral content did not play a major role. Thus, the quantitative changes in aging bone tissue, rather than the qualitative changes, influence the mechanical competence of the bone.

Related Papers

• → Effect of initial as-cast microstructure of AZ91D magnesium alloy on its semisolid microstructure(2010)20 cited
• → INTERSECTANT MICROSTRUCTURE OF HYDROXYAPATITE SHEETS OF SHANKBONE(2010)
• Analysis of Surface Layer Microstructure and Formation of Die Casting(2008)
• Influence of the Different Rolling Temperatures on Microstructures and Mechanical Properties of IMI550 Alloy Bars(2015)
• Effect of Heat Treatment on the Microstructure of Two-step Forging for High Nb Containing TiAl Alloy(2005)