Determination of Light Water Reactor Fuel Burnup with the Isotope Ratio Method

Citations Over Time

Abstract

For the current project to demonstrate that isotope ratio measurements can be extended to zirconium alloys used in LWR fuel assemblies we report new analyses on irradiated samples obtained from a reactor. Zirconium alloys are used for structural elements of fuel assemblies and for the fuel element cladding. This report covers new measurements done on irradiated and unirradiated zirconium alloys, Unirradiated zircaloy samples serve as reference samples and indicate starting values or natural values for the Ti isotope ratio measured. New measurements of irradiated samples include results for 3 samples provided by AREVA. New results indicate: 1. Titanium isotope ratios were measured again in unirradiated samples to obtain reference or starting values at the same time irradiated samples were analyzed. In particular, 49Ti/48Ti ratios were indistinguishably close to values determined several months earlier and to expected natural values. 2. 49Ti/48Ti ratios were measured in 3 irradiated samples thus far, and demonstrate marked departures from natural or initial ratios, well beyond analytical uncertainty, and the ratios vary with reported fluence values. The irradiated samples appear to have significant surface contamination or radiation damage which required more time for SIMS analyses. 3. Other activated impurity elements still limit the sample size for SIMS analysis of irradiated samples. The sub-samples chosen for SIMS analysis, although smaller than optimal, were still analyzed successfully without violating the conditions of the applicable Radiological Work Permit

Related Papers

• Effect of Nb and Fe on Corrosion Resistance of Zirconium Alloys(2010)
• PROPERTIES AND PROCESSING OF ZIRCONIUM AND ZIRCONIUM ALLOYS(1959)
• → Automatic System for Measuring the Zirconium Liner and Zircaloy-2 Thickness of Zirconium Liner Tubes(1989)
• → Measurement of impurity diffusion into the liner of a zirconium-lined zircaloy-2 tube(1990)
• → Study on zirconium alloys(1957)