Parametric effects on glass reaction in the unsaturated test method
Citations Over Time
Abstract
The Unsaturated Test Method has been applied to study glass reaction under conditions that may be present at the potential Yucca Mountain site, currently under evaluation for storage of reprocessed high-level nuclear waste. The results from five separate sets of parametric experiments are presented wherein test parameters ranging from water contact volume to sensitization of metal in contact with the glass were examined. The most significant effect was observed when the volume of water, as controlled by the water inject volume and interval period, was such to allow exfoliation of reacted glass to occur. The extent of reaction was also influenced to a lesser extent by the degree of sensitization of the 304L stainless steel. For each experiment, the release of cations from the glass and alteration of the glass were examined. The major alteration product is a smectite clay that forms both from precipitation from solution and from in-situ alteration of the glass itself. It is this clay that undergoes exfoliation as water drips from the glass. A comparison is made between the results of the parametric experiments with those of static leach tests. In the static tests the rates of release become progressively reduced through 39 weeks while, in contrast, they remain relatively constant in the parametric experiments for at least 300 weeks. This differing behavior may be attributable to the dripping water environment where fresh water is periodically added and where evaporation can occur.
Related Papers
- → Effects of SiC contents on the microstructure and mechanical properties of Al4SiC4–SiC ceramic composites(2023)6 cited
- → Nanocrystalline NiAl-TiC Composites Sintered by the Pulse Plasma Method(2006)1 cited
- → Elevated temperature compressive properties of reaction milled NiAl–AlN and Zr-doped NiAl–AlN composites(1992)13 cited
- → Porous SiC Ceramics with Multiple Pore Structure Fabricated via Gelcasting and Solid State Sintering(2016)
- → Retracted: XRD Peak Profile Analysis of SiC Reinforced Al2O3 Ceramic Composite Synthesized by Electrical Resistance Heating and Microwave Sintering: A Comparison(2023)