Overview of low temperature sensitization
Citations Over Time
Abstract
A review of the literature on low temperature sensitization (LTS) has been conducted to determine if LTS-related microstructural changes can occur in Type 304L stainless steel within the times and temperatures associated with nuclear waste storage. It was found that Type 304L stainless steel is susceptible to sensitization and LTS, and that cold work plays an important role in determining the rate of LTS. Severely cold worked Type 304L stainless steel would clearly develop LTS-related microstructural changes within the times and temperatures associated with nuclear waste storage. These changes could lead to increased susceptibility to corrosion. Significant improvements in the long-term resistance to sensitization, LTS and corrosion can be achieved by modest changes in alloy composition and fabrication practices. Therefore, Type 304L would not be the preferred alloy of construction for nuclear waste storage canisters. The final qualification of an alternate canister alloy should involve corrosion experiments on actual canisters. Suggestions for alternate canister alloys are 316L, 316LN, 316ELC, 347, and XM-19. 47 references, 4 figures.
Related Papers
- → Effect of Er on Microstructure and Corrosion Behavior of Al–Zn–Mg–Cu–Sc–Zr Aluminum Alloys(2022)15 cited
- → Corrosion resistance of TiAl–Nb coating on 316L stainless steel in liquid zinc(2020)7 cited
- Effect of Alloy Elements on the Alkali-Corrosion Resistance of Rare Earth Low Alloy Cast Iron(2008)
- The influences of Zn、Sb、Ti、Zr on the corrosion of ZL114A alloy(2008)
- The influences of alloying elements on the corrosion properties of as-cast Al-Si alloy(2007)