Strongly Confined CsPbBr3 Quantum Dots as Quantum Emitters and Building Blocks for Rhombic Superlattices
Citations Over TimeTop 10% of 2023 papers
Abstract
The success of the colloidal semiconductor quantum dots (QDs) field is rooted in the precise synthetic control of QD size, shape, and composition, enabling electronically well-defined functional nanomaterials that foster fundamental science and motivate diverse fields of applications. While the exploitation of the strong confinement regime has been driving commercial and scientific interest in InP or CdSe QDs, such a regime has still not been thoroughly explored and exploited for lead-halide perovskite QDs, mainly due to a so far insufficient chemical stability and size monodispersity of perovskite QDs smaller than about 7 nm. Here, we demonstrate chemically stable strongly confined 5 nm CsPbBr3 colloidal QDs via a postsynthetic treatment employing didodecyldimethylammonium bromide ligands. The achieved high size monodispersity (7.5% ± 2.0%) and shape-uniformity enables the self-assembly of QD superlattices with exceptional long-range order, uniform thickness, an unusual rhombic packing with an obtuse angle of 104°, and narrow-band cyan emission. The enhanced chemical stability indicates the promise of strongly confined perovskite QDs for solution-processed single-photon sources, with single QDs showcasing a high single-photon purity of 73% and minimal blinking (78% "on" fraction), both at room temperature.
Related Papers
- → New method of controlling the gaps between the minibands of a superlattice(1989)31 cited
- → The dynamic theory of X-ray diffraction by the one-dimensional ideal superlattice. II. Calculation of structure factors for some superlattice models(1985)13 cited
- → Disc-shaped nanocrystal model for simulating the diffraction peak profile from a one-dimensional superlattice and its application to Pt/AlN superlattice films(2016)2 cited
- → Very high quality p-type AlxGa1−xN/GaN superlattice(2002)11 cited
- → On the Fe-Cr Superlattice(1951)1 cited