Composition-Structure Relationships in the Li-Ion Battery Electrode Material LiNi0.5Mn1.5O4
Citations Over TimeTop 1% of 2012 papers
Abstract
A study of the correlations between the stoichiometry, secondary phases and transition metal ordering of LiNi(0.5)Mn(1.5)O(4) was undertaken by characterizing samples synthesized at different temperatures. Insight into the composition of the samples was obtained by electron microscopy, neutron diffraction and X-ray absorption spectroscopy. In turn, analysis of cationic ordering was performed by combining neutron diffraction with Li MAS NMR spectroscopy. Under the conditions chosen for the synthesis, all samples systematically showed an excess of Mn, which was compensated by the formation of a secondary rock salt phase and not via the creation of oxygen vacancies. Local deviations from the ideal 3:1 Mn:Ni ordering were found, even for samples that show the superlattice ordering by diffraction, with different disordered schemes also being possible. The magnetic behavior of the samples was correlated with the deviations from this ideal ordering arrangement. The in-depth crystal-chemical knowledge generated was employed to evaluate the influence of these parameters on the electrochemical behavior of the materials.
Related Papers
- → New method of controlling the gaps between the minibands of a superlattice(1989)31 cited
- → The dynamic theory of X-ray diffraction by the one-dimensional ideal superlattice. II. Calculation of structure factors for some superlattice models(1985)13 cited
- → Disc-shaped nanocrystal model for simulating the diffraction peak profile from a one-dimensional superlattice and its application to Pt/AlN superlattice films(2016)2 cited
- → Very high quality p-type AlxGa1−xN/GaN superlattice(2002)11 cited