Influence of Water on the Structure and Properties of PDMS-Containing Multiblock Polyurethanes

Citations Over TimeTop 10% of 2012 papers

Abstract

Segmented polyurethane multiblock polymers containing polydimethylsiloxane and polyether soft segments form tough and easily processed thermoplastic elastomers. Two commercially available examples, Elast-Eon E2A (denoted as E2A) and PurSil 35 (denoted as P35), were evaluated for molecular and mechanical stability after immersion in buffered water for up to 52 weeks at temperatures ranging from 37 to 85 °C. Dynamic mechanical spectroscopy experiments, performed in tension and shear, were used to characterize the linear viscoelastic properties of compression-molded (dry) specimens. Small-angle X-ray scattering measurements indicated a disorganized microphase-separated morphology for all test conditions. Upon aging in phosphate buffered saline, samples of E2A and P35 were analyzed by size exclusion chromatography (SEC) and tensile testing as a function of time and temperature. The absolute molar mass of each material prior to aging in water was determined by SEC using a multiangle light scattering detector. Aging at 85 °C and 52 weeks lead to a 67% and 50% reduction in molar mass from the original values for E2A and P35, respectively. We attribute the reduction in molar mass to hydrolysis of the polymer backbone and have evaluated the data using a pseudo-zero-order kinetics analysis. The temperature dependence of the extracted rate data is consistent with an activated (i.e., Arrhenius) process, and thus all the molar mass reduction data can be reduced to a single master curve. Concomitant with the reduction in molar mass, E2A and P35 transformed with aging from strain-hardening to strain-softening materials, characterized by substantially reduced tensile strength (stress at failure) and ultimate elongation (strain at failure) relative to the original properties.

Related Papers

• → An SEC/MALS study of alternan degradation during size-exclusion chromatographic analysis(2009)60 cited
• → Hydrodynamic versus Size Exclusion Chromatography Characterization of Alternan and Comparison to Off-Line MALS(2010)48 cited
• → Molar mass distribution by size exclusion chromatography: Comparison of multi‐angle light scattering and universal calibration(2019)20 cited
• → Strategy to improve the characterization of chitosan by size exclusion chromatography coupled with multi angle laser light scattering(2018)20 cited
• → Test Method for Determining the Molar Mass of Chitosan and Chitosan Salts by Size Exclusion Chromatography with Multi-angle Light Scattering Detection (SEC-MALS)(2008)