Infrared spectroscopic analysis of the Si/SiO2 interface structure of thermally oxidized silicon
Citations Over TimeTop 1% of 2000 papers
Abstract
The nature of the silicon oxide transition region in the vicinity of the Si/SiO2 interface is probed by infrared and x-ray photoelectron spectroscopies. The layer-by-layer composition of the interface is evaluated by uniformly thinning thermal oxide films from 31 Å down to 6 Å. We find that the thickness dependence of the frequencies of the transverse optical and longitudinal optical phonons of the oxide film cannot be reconciled by consideration of simple homogeneous processes such as image charge effects or stress near the interface. Rather, by applying the Bruggeman effective medium approximation, we show that film inhomogeneity in the form of substoichiometric silicon oxide species accounts for the observed spectral changes as the interface is approached. The presence of such substoichiometric oxide species is supported by the thickness dependence of the integrated Si suboxide signal in companion x-ray photoelectron spectra.
Related Papers
- → High reactivity of silicon suboxide clusters(2001)62 cited
- → Structure and hydrogen generation mechanism of Si-based agent(2020)14 cited
- → Structures and Properties of Silicon Oxide Clusters by Theoretical Investigations(2006)21 cited
- → Estimation of the Thickness of Ultrathin Silicon Nitride Films by X-Ray Photoelectron Spectroscopy(1993)9 cited
- → Characterization of Si Nanocrystals Embedded in SiO<sub>2</sub> with X-Ray Photoelectron Spectroscopy(2005)